Vestamid® L-GF15 23% Glass Filled Nylon 12 | Metasan
Home
/
Products
/
Polyamides
/
Glass fiber
/ Vestamid® L-GF15 23% Glass Filled Nylon 12
Vestamid® L-GF15 23% Glass Filled Nylon 12
این ماده گریدی از نایلون بوده که حاوی کمک فرآیند و 15% الیاف شیشه خرد شده است و ویسکوزیته متوسطی دارد.
Packaging
Price unavailable
Unit price
Price inquiry required
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
بدنه جعبه دنده در بالابر شیشه خودرو
Advantages
پایداری حرارتی خوب
Reviews
No reviews yet.
Submit review
Full name
Email
Your review
Submit review
Specifications
Property
Value
Unit
Electrical Properties
Comparative Tracking Index
>600
Test Solution A, 50 drops; IEC 60112
V
Dielectric Constant
4
IEC 60250@Frequency 100 Hz
Dissipation Factor
0.26
IEC 60250@Frequency 1e+6 Hz
Volume resistance
1,000,000,000,000,000
IEC 60093
ohm-cm
Dielectric Strength
44
K20/P50; IEC 60243-1
kV/mm
Dielectric Constant
3.4
IEC 60250@Frequency 1e+6 Hz
Dissipation Factor
0.038
IEC 60250@Frequency 100 Hz
Comparative Tracking Index
600
Test Solution A, 100 drops; IEC 60112
V
Chemical Properties
Electrolytic Corrosion
A1 Step
IEC 60426
Water absorption
1.3
ISO 62-at Saturation@Thickness 1.00 mm
%
Thermal Properties
Vicat softening temperature
175
10N; ISO 306
°C
Heat Deflection temperature
160
ISO 75- at 1.8 MPa
°C
Flameability
HB
@Thickness 1.60 mm
Thermal Expansion
80
45x15x10 mm; ISO 11359@Temperature 23.0 -55.0 °C
um/(m-°C)
Heat Deflection temperature
175
ISO 75- at 0.46 MPa
°C
Flameability
V-2
@Thickness 3.20 mm
Vicat softening temperature
170
50N; ISO 306
°C
Physical Properties
Melting point
178
Peak Temperature; ISO 3146, ISO 11357
°C
Moisture absorption
0.6
50% R.H.; ISO 62 @Thickness 1.00 mm, Temperature 23.0 °C, at Equilibrium
%
Density
1.12
ISO 1183
g/mL
Processing Properties
Linear Mold Shrinkage
0.011
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2), Transverse
cm/cm
Linear Mold Shrinkage
0.001
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2)
cm/cm
Mechanical Properties
Elongation at break-MD
6
ISO 527-1/2
%
Tensile modulus-MD
3,900
ISO 527-1/2
MPa
Tensile Stress at break-MD
95
ISO 527-1/2
MPa
(Charpy Impact Strength(unnotched
75
ISO 179/1eU@Temperature 23.0 °C
kJ/m2
Charpy Impact Strength (notched)
17
ISO 179/1eA@Temperature 23.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
80
ISO 179/1eU@Temperature -30.0 °C
kJ/m2
Charpy Impact Strength (notched)
11
ISO 179/1eA@Temperature -30.0 °C
kJ/m2