Dyflor® LE PVDF | Metasan
Home
/
Products
/
Fluoropolymers
/ Dyflor® LE PVDF
Dyflor® LE PVDF
Thermoplastic, low viscosity plastic resin for injection molding, compression molding and extrusion.
Packaging
Price unavailable
Unit price
Price unavailable
Producer
Delivery location
-
Minimum order
-
Order quantity
-
Request price
Additional Information
Applications
Wire and cable jacketing
Specifications
Property
Value
Unit
Mechanical Properties
Creep modulus
950
1000hours
MPa
Tensile Impact strength
140
kJ/m2
Charpy Impact Strength (notched)
6
@Temperature -30.0 °C
kJ/m2
(Charpy Impact Strength(unnotched
260
kJ/m2
Elongation at yield
8
%
Tensile modulus-MD
2,100
MPa
Tensile strength
55
MPa
Elongation at break-MD
>50
%
Creep modulus
1,600
1hour
MPa
Charpy Impact Strength (notched)
13
kJ/m2
(Charpy Impact Strength(unnotched
210
@Temperature -30.0 °C
kJ/m2
Electrical Properties
Comparative Tracking Index
275
V
Dissipation Factor
0.24
@Frequency 1e+6 Hz
Surface Resistance
>1.00e+15
ohm
Electrical Resistivity
30,000,000,000,000
ohm-cm
Dielectric Constant
8
@Frequency 1e+6 Hz
Dielectric Strength
22
kV/mm
Dissipation Factor
0.034
@Frequency 100 Hz
Dielectric Constant
9
@Frequency 100 Hz
Thermal Properties
Flameability
V-0
@Thickness 1.60 mm
Vicat softening temperature
166
50°C/hr/50 N
degC
Heat Deflection temperature
130
at 0.46 MPa
degC
Thermal Expansion
100
Transverse to Flow@Temperature 20.0 °C
um/(m-degC)
Heat Deflection temperature
70
at 1.8 MPa
degC
Thermal Expansion
100
Parallel to Flow@Temperature 20.0 °C
um/(m-degC)
Processing Properties
MFI
15
g/10min
Physical Properties
Density
1.78
g/mL
Chemical Properties
Water absorption
0
%