Specifications
PropertyValueUnit
Processing Properties
Drying Temperature160°C
MFI9.1380°C/5 kg- ISO 1133g/10min
Dry Time240min
Mold Temperature180°C
Physical Properties
Shrinkage1.1ISO 294-4, in transverse direction%
Density1.3ISO 1183- 23°Cg/mL
Melting point340ISO 11357, DSC, 2nd heating°C
Melting range370 – 380°C
Shrinkage0.9ISO 294-4, in flow direction%
Mechanical Properties
Charpy Impact Strength (notched)8ISO 179/1eA, -30°CkJ/m2
Tensile modulus-MD3,400ISO 527-1MPa
Tensile Stress at yield-MD95ISO 527-1MPa
Strain at break-MD40ISO 527-2%
(Charpy Impact Strength(unnotchedNBISO 179/1eU, -30°CkJ/m2
Charpy Impact Strength (notched)9ISO 179/1eA, 23°CkJ/m2
(Charpy Impact Strength(unnotchedNBISO 179/1eU, 23 °C
Thermal Properties
FlameabilityV-0 ClassUL94, 3.2 mm
Vicat softening temperature305ISO 306, 50N, Method A°C
Heat Deflection temperature1551.8 MPa°C
Heat Deflection temperature2050.45 MPa°C
Vicat softening temperature335ISO 306, 10N, Method A°C
Appearance Properties
Physical stateگرانول
Electrical Properties
Surface Resistance10^14IEC 60093ohm
Dielectric Strength16IEC 60243-1, K20/P50kV/mm
Comparative Tracking Index200IEC 60112V
Relative permittivity2.8IEC 60250, 1 MHz
Volume resistance10^15IEC 60093ohm-cm
Comparative Tracking Index175IEC 60112V